Elastic properties of Aryl-Ketone-Polymer (UAKP) and tensile bond strength (TBS) to denture resin (PalaXpress) were tested. Indentation modulus (EIT) and indentation hardness (HIT) were measured via Martens hardness (n=10 specimens) with 4.2±0.6 kN/mm2 and 261±8 N/mm2 respectively. TBS was tested in dependence of different adhesives (visio.link (VL), Adhese Universal (AU), All-Bond Universal (ABU), CLEARFIL UNIVERSAL BOND (CUB), G-Premio BOND (GPB), iBOND Universal (IBU), ONE COAT 7 UNIVERSAL (OCU), Scotchbond Universal (SBU) and without adhesive (CG), n=18/group) and the application of opaquer (n=9/group) after thermocycling (5°C/55°C, 10,000×). TBS was affected by the adhesive (η (P2=0.715, p<0.001) followed by the opaquer (ηP2=0.335, p<0.001). VL and CG showed highest TBS followed by AU and ABU. IBU and GPB resulted in lowest TBS. Opaquer increased TBS for all adhesives (p<0.05), except VL and CG (p<0.258). Elastic properties are well-suited for the indication of removable partial dentures. Bonding to denture resin is no limiting factor.