The present study deals with the effect of pre-deformation technique of AA2519 alloy (Al–5.64Cu–0.33Mn–0.23Mg–0.15Zr–0.11Ti–0.09V–0.08Fe–0.01Si (wt. %)) under T8 tempers, on condition that intermediate strains are equal. After undergoing T87 by pre-stretching and peak ageing the alloy demonstrates the yield stress, ultimate tensile strength and elongation to failure of 425.4±2.4 MPa, 475±2.4 MPa, 12.1±0.4%, respectively. The 7% pre-straining by rolling leads to-5% decrease in yield stress, practically the same ultimate tensile strength and-20% decrease in ductility. This effect can be ascribed to more homogeneous distribution of dislocations which act as heterogeneous nucleation sites for the θ′-phase precipitation. In addition to precipitates of the Al–Cu family (θ′′ and θ′), Ω-phase plates on {111}α habit plane was observed. The effect of pre-straining prior to ageing on the precipitation behavior and its relation with mechanical properties of the AA2519 is considered.