LAUSR

Background The purpose of this study was to evaluate the effect of aging process on the tensile strength (TS) of repaired acrylic denture base using ZrO2 nanoparticles (nano-ZrO2)-reinforced autopolymerized resin. Material and Methods A total of 240 heat-polymerized acrylic resin specimens (n=10) were prepared and sectioned creating 2 mm-repair-gap. Autopolymerized acrylic resin, pure and modified with 2.5, 5, and 7.5wt% nano-ZrO2 were used for specimens repair. TS of repaired specimens were measured using the universal testing machine after water immersion at 37oC for 2, 7 and 30 days. At each time interval, half the immersed specimens underwent thermo-cycling aging process (5000 cycles at 5/55°C) before TS testing. One-way ANOVA and Tukey-Kramer multiple-comparison tests were used for data analysis at α=0.05. Results Aging process for all groups showed significant differences in TS between unreinforced and nano-ZrO2 reinforced groups (p<0.05). Within immersed nano-ZrO2-reinforced specimens, 5% group immersed for 30-days showed the highest significant TS value (p<0.05). With regards to thermocycling, 5% group showed the highest TS values after 2-days and 30-days groups while after 7-days, significant differences were found between 2.5% group and 5% and 7.5% groups (p<0.05). SEM images analysis displayed the ductile fracture type for nano-ZrO2 reinforced groups. Conclusions In summary, 5.0%-nano-ZrO2 addition to repair resin showed an improvement in tensile strength of repaired acrylic resin with different aging processes. Key words:Acrylic resins, denture repair, tensile strength, thermocycling, water storage, zirconium oxide nanoparticle.