Environmentally assisted degradation of spinodal copper alloy C72900
Sign Up to like & getrecommendations! Published in 2018 at "Corrosion Science"
DOI: 10.1016/j.corsci.2018.06.031
Abstract: Abstract In this work, a spinodal Copper alloy – C72900, was tested to investigate the resistance against environmentally assisted degradation. The material was tested according to ISO 15156-3 Level V in sour H2S solution and… read more here.
Keywords: alloy c72900; copper; environmentally assisted; spinodal copper ... See more keywords
Relationship between microstructural features in pipeline steel and hydrogen assisted degradation
Sign Up to like & getrecommendations! Published in 2019 at "Engineering Failure Analysis"
DOI: 10.1016/j.engfailanal.2018.11.008
Abstract: Abstract The contributions of various microstructural features towards hydrogen-assisted degradation in API 5L X80 pipeline steel have been investigated. The current study was conducted on specimens obtained from the top surface and mid-thickness layers. After… read more here.
Keywords: hydrogen; top surface; hydrogen assisted; assisted degradation ... See more keywords