Suppression mechanism of initial pitting corrosion of pure Zn by Li alloying
Sign Up to like & getrecommendations! Published in 2021 at "Corrosion Science"
DOI: 10.1016/j.corsci.2021.109564
Abstract: Abstract Localized corrosion makes Zn vulnerable to unpredictable fracture under stress loading, resulting in mechanical failure when used as implants in human body. This study reveals that 0.8 wt.% Li alloying suppresses pitting corrosion of… read more here.