Critical current degradation and delamination crack observation of epoxy-coated REBCO superconducting tapes after thermal cycles in liquid nitrogen
Sign Up to like & getrecommendations! Published in 2021 at "Ceramics International"
DOI: 10.1016/j.ceramint.2021.07.155
Abstract: Abstract The delamination and critical current (Ic) degradation caused by thermal stress after epoxy impregnation are threats for the application of REBa2Cu3O7-x(REBCO, RE = Rare earth) superconducting magnets. In this work, two types of REBCO tapes were… read more here.