Bending behavior and damage evolution of GLARE laminate using in‐situ AE technology and FEM
Sign Up to like & getrecommendations! Published in 2024 at "Polymer Composites"
DOI: 10.1002/pc.28706
Abstract: GLARE laminate experiences multiple damage modes during bending failure, including fiber fracture, matrix cracking, interlayer delamination, and fracture of aluminum alloy. In most cases, two or more failure modes occur together, which makes the damage… read more here.